Dow Wire & Cable DGDA-1310 BK

About this Product

DGDA-1310 BK is a black HDPE jacket grade for both Power (MV and HV) and telecom cable applications. The material provides excellent mechanical and physical properties and environmental stress crack resistance in combination with good processability.

DGDA-1310 BK can be extruded using conventional cable jacket techniques with melt temperatures typically between 200 and 230 deg C.

Specifications.
DGDA-1310 BK meets the following Raw material specifications:

  • ASTM D 1248 Type III, Class C, Category 5, Grade J4, E8, E9, W8, W9
  • ISO 1872-PE, KHL, 50-D003

Cables jacketed with DGDA-1310 BK, using industry standard commercial extrusion practice, should meet the following cable specifications:

  • IEC 60502, ST 7
  • IEC 62067, ST 7
  • IEC 60840, ST 7
  • ICEA S-94 649
  • ICEA S-108 720
  • ICEA S-97 682
  • ICEA-S-87-640
  • BS 6234: Type H03C, TS2
  • Telcordia GR-70-CORE
  • HD 620 S2, Part 1, Table 4B, type DMP2, DMP 9-10, DMP 14-15, DMP 17
  • EN 50290-2-24
Brand: Dow Wire & CableProducer: DowPolymer Type: HDPEFiller: 2.5% Carbon PowderQuality: PrimeForm: GranulesSustainability: Not Classified
Abrasion Resistant
ESCR (Stress Crack Resist.), High
Friction, Low
High Voltage
Jacketing
Medium Voltage
Telecoms
UV Stabilized

Markets and Technologies


Specifications

-D 1248, III, Class C, Cat. 5
-6234 Type H03C, TS2
-50290-2-24
-620 S2, Part 1, Table 4B, type DMP2, DMP 9-10, DMP 14-15, DMP 17
-S-108-720
-S-87-640
-S-94-649
-S-97-682
-60502 Type ST7
-60840
-62067
-1872 PE KHL 50D003

Request Quote

Fast response
Requesting quotations is exclusive to selected users. Please login or register. New to our platform? Sign up, follow the provided instructions, and get verified to access our services.
Personalised Products & PricingRequest quotes for specific grades and quantities quickly.
Comprehensive Material InformationAccess detailed information for our entire product range.
Efficient Order ManagementTrack the status of your orders and retrieve detailed information.

Related Documents

0 documents found